Properti fisik |
Metrik |
Bahasa inggris |
Komentar |
Kepadatan |
2,81 g/cc |
0,102 pon/in³ |
A A;Khas |
|
Peralatan mekanis |
Metrik |
Bahasa inggris |
Komentar |
Kekerasan, Brinell |
150 |
150 |
A A;Khas;beban 500 g;bola 10 mm |
Kekerasan, Knoop |
191 |
191 |
Dikonversi dari Nilai Kekerasan Brinell |
Kekerasan, Rockwell A |
53.5 |
53.5 |
Dikonversi dari Nilai Kekerasan Brinell |
Kekerasan, Rockwell B |
87 |
87 |
Dikonversi dari Nilai Kekerasan Brinell |
Kekerasan, Vickers |
175 |
175 |
Dikonversi dari Nilai Kekerasan Brinell |
Kekuatan Tarik, Ultimate |
572 MPa |
83000psi |
A A;Khas |
|
41,0 MPa @Suhu 371 °C |
5950psi @Suhu 700 °F |
|
|
55,0 MPa @Suhu 316 °C |
7980psi @Suhu 601 °F |
|
|
76,0 MPa @Suhu 260 °C |
11000psi @Suhu 500 °F |
|
|
110 MPa @Suhu 204 °C |
16000psi @Suhu 399 °F |
|
|
214 MPa @Suhu 149 °C |
31000psi @Suhu 300 °F |
|
|
483 MPa @Suhu 100 °C |
70100psi @Suhu 212 °F |
|
|
572 MPa @Suhu 24.0 °C |
83000psi @Suhu 75,2 °F |
|
|
593 MPa @Suhu -28.0 °C |
86000psi @Suhu -18,4 °F |
|
|
621 MPa @Suhu -80.0 °C |
90100psi @Suhu -112 °F |
|
|
703 MPa @Suhu -196 °C |
102000psi @Suhu -321 °F |
|
|
>= 462 MPa @Ketebalan 88,93 - 102 mm |
>= 67000 psi @Ketebalan 3,501 - 4,00 inci |
Piring;T62, T651 |
|
>= 490 MPa @Ketebalan 76,23 - 88,9 mm |
>= 71100 psi @Ketebalan 3,001 - 3,50 inci |
Piring;T62, T651 |
|
>= 496 MPa @Ketebalan 63,53 - 76,2 mm |
>= 71900 psi @Ketebalan 2,501 - 3,00 inci |
Piring;T62, T651 |
|
>= 510 MPa @Ketebalan 0,203 - 0,279 mm |
>= 74000 psi @Ketebalan 0,00800 - 0,0110 inci |
Lembaran |
|
>= 524 MPa @Ketebalan 0,305 - 0,991 mm |
>= 76000 psi @Ketebalan 0,0120 - 0,0390 inci |
Lembaran |
|
>= 524 MPa @Ketebalan 50,83 - 63,5 mm |
>= 76000 psi @Ketebalan 2,001 - 2,50 inci |
Piring;T62, T651 |
|
>= 531 MPa @Ketebalan 25,43 - 50,8 mm |
>= 77000 psi @Ketebalan 1,001 - 2,00 inci |
Piring;T62, T651 |
|
>= 538 MPa @Ketebalan 1,02 - 3,17 mm |
>= 78000 psi @Ketebalan 0,0400 - 0,125 inci |
Lembaran |
|
>= 538 MPa @Ketebalan 3,20 - 6,32 mm |
>= 78000 psi @Ketebalan 0,126 - 0,249 inci |
Lembaran |
|
>= 538 MPa @Ketebalan 6,35 - 12,7 mm |
>= 78000 psi @Ketebalan 0,250 - 0,499 inci |
Piring;T62, T651 |
|
>= 538 MPa @Ketebalan 12,7 - 25,4 mm |
>= 78000 psi @Ketebalan 0,500 - 1,00 inci |
Piring;T62, T651 |
Kekuatan Tarik, Hasil |
503 MPa |
73000psi |
A A;Khas |
|
>= 372 MPa @Ketebalan 88,93 - 102 mm |
>= 54000 psi @Ketebalan 3,501 - 4,00 inci |
Piring;T62, T651 |
|
>= 400 MPa @Ketebalan 76,23 - 88,9 mm |
>= 58000 psi @Ketebalan 3,001 - 3,50 inci |
Piring;T62, T651 |
|
>= 421 MPa @Ketebalan 63,53 - 76,2 mm |
>= 61100 psi @Ketebalan 2,501 - 3,00 inci |
Piring;T62, T651 |
|
>= 434 MPa @Ketebalan 0,203 - 0,279 mm |
>= 62900 psi @Ketebalan 0,00800 - 0,0110 inci |
Lembaran |
|
>= 441 MPa @Ketebalan 50,83 - 63,5 mm |
>= 64000 psi @Ketebalan 2,001 - 2,50 inci |
Piring;T62, T651 |
|
>= 462 MPa @Ketebalan 0,305 - 0,991 mm |
>= 67000 psi @Ketebalan 0,0120 - 0,0390 inci |
Lembaran |
|
>= 462 MPa @Ketebalan 6,35 - 12,7 mm |
>= 67000 psi @Ketebalan 0,250 - 0,499 inci |
Piring;T62, T651 |
|
>= 462 MPa @Ketebalan 25,43 - 50,8 mm |
>= 67000 psi @Ketebalan 1,001 - 2,00 inci |
Piring;T62, T651 |
|
>= 469 MPa @Ketebalan 1,02 - 3,17 mm |
>= 68000 psi @Ketebalan 0,0400 - 0,125 inci |
Lembaran |
|
>= 469 MPa @Ketebalan 12,7 - 25,4 mm |
>= 68000 psi @Ketebalan 0,500 - 1,00 inci |
Piring;T62, T651 |
|
>= 476 MPa @Ketebalan 3,20 - 6,32 mm |
>= 69000 psi @Ketebalan 0,126 - 0,249 inci |
Lembaran |
|
32,0 MPa @ Saring 0,200 %, Suhu 271 °C |
4640psi @ Saring 0,200 %, Suhu 520 °F |
|
|
45,0 MPa @ Saring 0,200 %, Suhu 316 °C |
6530psi @ Saring 0,200 %, Suhu 601 °F |
|
|
62,0 MPa @ Saring 0,200 %, Suhu 260 °C |
8990psi @ Saring 0,200 %, Suhu 500 °F |
|
|
87,0 MPa @ Saring 0,200 %, Suhu 204 °C |
12600psi @ Saring 0,200 %, Suhu 399 °F |
|
|
186 MPa @ Saring 0,200 %, Suhu 149 °C |
27000psi @ Saring 0,200 %, Suhu 300 °F |
|
|
448 MPa @ Saring 0,200 %, Suhu 100 °C |
65000psi @ Saring 0,200 %, Suhu 212 °F |
|
|
503 MPa @ Saring 0,200 %, Suhu 24.0 °C |
73000psi @ Saring 0,200 %, Suhu 75,2 °F |
|
|
517 MPa @ Saring 0,200 %, Suhu -28.0 °C |
75000psi @ Saring 0,200 %, Suhu -18,4 °F |
|
|
545 MPa @ Saring 0,200 %, Suhu -80.0 °C |
79000psi @ Saring 0,200 %, Suhu -112 °F |
|
|
634 MPa @ Saring 0,200 %, Suhu -196 °C |
92000psi @ Saring 0,200 %, Suhu -321 °F |
|
Perpanjangan saat Putus |
9,0% @Suhu -196 °C |
9,0% @Suhu -321 °F |
|
|
11% @Suhu -80.0 °C |
11% @Suhu -112 °F |
|
|
11% @Suhu -28.0 °C |
11% @Suhu -18,4 °F |
|
|
11% @Suhu 24.0 °C |
11% @Suhu 75,2 °F |
|
|
14% @Suhu 100 °C |
14% @Suhu 212 °F |
|
|
30% @Suhu 149 °C |
30% @Suhu 300 °F |
|
|
55 % @Suhu 204 °C |
55 % @Suhu 399 °F |
|
|
65% @Suhu 260 °C |
65% @Suhu 500 °F |
|
|
70% @Suhu 316 °C |
70% @Suhu 601 °F |
|
|
70% @Suhu 371 °C |
70% @Suhu 700 °F |
|
|
>= 3,0% @Ketebalan 88,93 - 102 mm |
>= 3,0% @Ketebalan 3,501 - 4,00 inci |
Piring;T62, T651 |
|
>= 5,0% @Ketebalan 0,203 - 0,279 mm |
>= 5,0% @Ketebalan 0,00800 - 0,0110 inci |
Lembaran |
|
>= 5,0% @Ketebalan 50,83 - 63,5 mm |
>= 5,0% @Ketebalan 2,001 - 2,50 inci |
Piring;T62, T651 |
|
>= 5,0% @Ketebalan 63,53 - 76,2 mm |
>= 5,0% @Ketebalan 2,501 - 3,00 inci |
Piring;T62, T651 |
|
>= 5,0% @Ketebalan 76,23 - 88,9 mm |
>= 5,0% @Ketebalan 3,001 - 3,50 inci |
Piring;T62, T651 |
|
>= 6,0% @Ketebalan 25,43 - 50,8 mm |
>= 6,0% @Ketebalan 1,001 - 2,00 inci |
Piring;T62, T651 |
|
>= 7,0% @Ketebalan 0,305 - 0,991 mm |
>= 7,0% @Ketebalan 0,0120 - 0,0390 inci |
Lembaran |
|
>= 7,0% @Ketebalan 12,7 - 25,4 mm |
>= 7,0% @Ketebalan 0,500 - 1,00 inci |
Piring;T62, T651 |
|
>= 8,0% @Ketebalan 1,02 - 3,17 mm |
>= 8,0% @Ketebalan 0,0400 - 0,125 inci |
Lembaran |
|
>= 8,0% @Ketebalan 3,20 - 6,32 mm |
>= 8,0% @Ketebalan 0,126 - 0,249 inci |
Lembaran |
|
>= 9,0% @Ketebalan 6,35 - 12,7 mm |
>= 9,0% @Ketebalan 0,250 - 0,499 inci |
Piring;T62, T651 |
|
11% @Ketebalan 1,59 mm |
11% @Ketebalan 0,0625 inci |
A A;Khas |
|
11% @Diameter 12,7 mm |
11% @Diameter 0,500 inci |
A A;Khas |
Modulus Elastisitas |
71,7 GPa |
10400 ksi |
A A;Khas;Rata-rata ketegangan dan kompresi.Modulus kompresi sekitar 2% lebih besar dari modulus tarik. |
Rasio Poison |
0,33 |
0,33 |
|
Kekuatan kelelahan |
159 MPa @# Siklus 5.00e+8 |
23000psi @# Siklus 5.00e+8 |
stres yang sepenuhnya terbalik;Mesin/spesimen RR Moore |
Ketangguhan patah |
17,6 MPa-m½ |
16,0 ksi-in½ |
T651;Piring;SL;rata-rata |
|
16,5 - 19,8 MPa-m½ |
15,0 - 18,0 ksi-in½ |
T651;Piring;SL |
|
18,7 MPa-m½ |
17,0 ksi-in½ |
T651;Tempa;SL |
|
20,0 MPa-m½ |
18,2 ksi-in½ |
K(IC) dalam Arah SL |
|
22,0 - 25,3 MPa-m½ |
20,0 - 23,0 ksi-in½ |
T651;Piring;TL |
|
24,2 MPa-m½ |
22,0 ksi-in½ |
T651;Piring;TL;rata-rata |
|
25,0 MPa-m½ |
22,8 ksi-in½ |
K(IC) dalam Arah TL |
|
28,6 MPa-m½ |
26,0 ksi-in½ |
T651;Piring;LT;rata-rata |
|
27,5 - 29,7 MPa-m½ |
25,0 - 27,0 ksi-in½ |
T651;Piring;LT |
|
29,0 MPa-m½ |
26,4 ksi-in½ |
K(IC) dalam Arah LT |
Kemampuan mesin |
70% |
70% |
0-100 Skala Paduan Aluminium |
Modulus geser |
26,9 GPa |
3900 ksi |
|
Kekuatan Geser |
331 MPa |
48000psi |
A A;Khas |
|
Properti Listrik |
Metrik |
Bahasa inggris |
Komentar |
Resistivitas Listrik |
0,00000515 ohm-cm @Suhu 20.0 °C |
0,00000515 ohm-cm @Suhu 68.0 °F |
A A;Khas |
|
Properti Termal |
Metrik |
Bahasa inggris |
Komentar |
CTE, linier |
21,6 µm/m-°C @Suhu -50.0 - 20.0 °C |
12,0 µin/dalam-°F @Suhu -58.0 - 68.0 °F |
|
|
23,4 µm/m-°C @Suhu 20.0 - 100 °C |
13,0 µin/dalam-°F @Suhu 68,0 - 212 °F |
|
|
23,6 µm/m-°C @Suhu 20.0 - 100 °C |
13,1 µin/dalam-°F @Suhu 68,0 - 212 °F |
A A;Khas;rata-rata di atas jangkauan |
|
24,3 µm/m-°C @Suhu 20.0 - 200 °C |
13,5 µin/dalam-°F @Suhu 68,0 - 392 °F |
|
|
25,2 µm/m-°C @Suhu 20.0 - 300 °C |
14,0 µin/dalam-°F @Suhu 68.0 - 572 °F |
|
Kapasitas panas spesifik |
0,960 J/g-°C |
0,229 BTU/lb-°F |
|
Konduktivitas termal |
130 W/mK |
900 BTU-dalam/jam-ft²-°F |
A A;Khas pada 77°F |
Titik lebur |
477 - 635.0 °C |
890 - 1175 °F |
A A;Rentang tipikal berdasarkan komposisi tipikal untuk produk tempa dengan ketebalan >= 1/4 in.Homogenisasi dapat meningkatkan suhu leleh eutektik sebesar 20-40°F tetapi biasanya tidak menghilangkannya. |
Solidus |
477 °C |
890 °F |
A A;Khas |
Likuidus |
635,0 °C |
1175 °F |
A A;Khas |
|
Properti Pemrosesan |
Metrik |
Bahasa inggris |
Komentar |
Suhu Anil |
413 °C |
775 °F |
|
Suhu larutan |
466 - 482 °C |
870 - 900 °F |
|
Suhu Penuaan |
121 °C |
250 °F |
|